| This material complies with recommendations & statutory regulations in the USA, Japan and most European countries regarding packaging materials intended to come in contact with foodstuff.&& |
| Product Description | |
|---|---|
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Smoothness,Optical performance,High anti-blocking,Butylene copolymer |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 6.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | 0.11 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| tensile strength | ASTM D882 | ||
| MD, fracture, 30 µ m | 30.0 | MPa | ASTM D882 |
| TD, fracture, 30 µ m | 18.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 30 µ m | 900 | % | ASTM D882 |
| TD, fracture, 30 µ m | 800 | % | ASTM D882 |
| Drop hammer impact | |||
| 30 µm | 75 | g | ASTM D1709 |
| tear strength | ASTM D1922 | ||
| MD，30 µm | 44.1 | kN/m | ASTM D1922 |
| TD，30 µm | 98.1 | kN/m | ASTM D1922 |
| Blocking force | |||
| 30.0 µm | 69.0 | g/100 cm² | ASTM D3354 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 104 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，30 µm | 110 | ASTM D2457 | |
| transparency | |||
| 30.0 µm | 72.0 | ASTM D1746 | |
| Haze | |||
| 30 µm | 6.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 170 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |