| About |
|---|
| Product Description | |
|---|---|
| Supplier | Marplex |
| Generic | PC+ABS |
| Material Status | Commercial: Negative |
| Availabilitys | North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 2.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.25 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 400 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | 98 | ℃ | ASTM D648 |
| Vicat Softening Temp | 134 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD | 7.2E-5 | 1/K | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 114 | ASTM D785 | |
| tensile strength | |||
| 3.20 mm | 53.0 | MPa | ASTM D638 |
| Tensile strain | 60 | % | ASTM D638 |
| Bending modulus | 2400 | MPa | ASTM D790 |
| bending strength | 86 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 95 to 100 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Temperature at the rear of the barrel | 225 to 240 | °C | |
| Temperature in the middle of the barrel | 230 to 245 | °C | |
| Front temperature of material barrel | 235 to 250 | °C | |
| Processing (melt) temperature | 235 to 245 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Injection pressure | 60.0 to 140 | MPa | |
| Injection speed | 中等 | ||
| Back pressure | 0.100 to 0.500 | MPa | |
| Screw speed | 40 to 60 | rpm | |
| Locking force | 4.0 to 8.0 | kN/cm² | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |