| ASTALOY™ PC/ABS M130S is a high melt flow alloy of ABS and Polycarbonate and is designed for long flow path injection moulding applications requiring a balance of impact toughness, product rigidity, heat resistance and mouldability. Typical automotive applications include painted exterior body panels, instrument panel substrates, remote locking keypads and tailgate upper air deflectors. Note: The letters “U” or “W” indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS M130SU ].&& |
| Product Description | |
|---|---|
| Supplier | Marplex |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,High impact resistance,High liquidity,Sprayable,Heat Resistance, Good,HB |
| Availabilitys | North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，3.80kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.0 mm | 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.25 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 630 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 3.2 mm | 55.0 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.2 mm | 98.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 100 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 12.7 mm | 106 | ℃ | ASTM D648 |
| Vicat Softening Temp | 132 | ℃ | ASTM D1525 4 |
| Linear coefficient of thermal expansion | |||
| MD | 7.2E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Igniting temperature of the hot wire | |||
| 1.6 mm | 550 | ℃ | AS/NZS 60695.2.12 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| tensile strength | |||
| 3.20 mm | 55.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 100 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2400 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 85.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 to 100 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Barrel rear temperature | 235 to 255 | °C | |
| Barrel middle temperature | 245 to 265 | °C | |
| Barrel front temperature | 255 to 275 | °C | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 50 to 90 | °C | |
| Injection pressure | 60.0 to 140 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.051 in/min |
| 4. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |