| A low density polyethylene resin well suited for extrusion coating and lamination applications. This resin has excellent adhesion and low neck-in at high speeds.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Low shrinkage,Good bond |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.916 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 12 | g/10min | ASTM D1238 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 89.0 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 94 | ASTM D2240 | |
| Shaw’s D | 47 | ASTM D2240 | |
| tensile strength | |||
| fracture | 9.50 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 500 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 202 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 280 to 320 | °C | |
| Maximum line speed | 7.6 | m/sec | |
| Minimum coating thickness 3 | 5.0 | µm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |