| This is a multi-purpose resin commonly used for flexible packaging coextrusion to provide superior sealability, opticals, and strength, high quality microcellular crosslinked foam, extrusion, injection molding, and tubing applications.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Optical performance,Copolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.931 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.8 | g/10min | ASTM D1238 |
| Vinyl acetate content | 9.0 | wt% | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| 1% secant | 101 | MPa | ASTM D790 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture | 18.0 | MPa | ASTM D882A |
| MD, fracture | 17.0 | MPa | ASTM D882A |
| Tensile strain | |||
| TD, fracture | 600 | % | ASTM D882A |
| MD, fracture | 400 | % | ASTM D882A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 81.0 | ℃ | ASTM D1525 |
| Melting peak temperature | 101 | ℃ | ASTM D3418 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | < 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |