| About |
|---|
| ATTANE™ 4606GC Ultra Low Density Ethylene/Hexene Copolymer is a skin layer in cast film offers excellent low temperature hot tack properties combined with outstanding tear and impact strength. In stretch film applications, ATTANE™ 4606GC Ultra Low Density Ethylene/Hexene Copolymer Resin exhibits excellent stretchability as well as good physical and cling properties. ATTANE™ 4606GC Ultra Low Density Ethylene/Hexene Copolymer Resin can also be utilised in blown film coextrusion where it is combined with other resins having excellent bubble stability allowing ATTANE™ 4606GC Ultra Low Density Ethylene/Hexene Copolymer Resin to be used as a sealant in multilayer film structures. Applications: Cling layer in cast stretch film Sealants in cast and blown films Complies with: Europe Commission Regulation (EU), No 10/2011 U.S. FDA FCN 741 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | VLDPE |
| Material Status | Commercial: Negative |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.911 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.3 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 23 | µm | |
| Membrane puncture strength | |||
| 23 µm | 2.80 | J | ASTM D5748 |
| Membrane puncture force | |||
| 23 µm | 35.0 | N | ASTM D5748 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 23 µ m | 4.80 | MPa | ISO 527-3 |
| TD, yield, 23 µ m | 4.50 | MPa | ISO 527-3 |
| MD, fracture, 23 µ m | 28.0 | MPa | ISO 527-3 |
| TD, fracture, 23 µ m | 25.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 23 µ m | 450 | % | ISO 527-3 |
| TD, fracture, 23 µ m | 600 | % | ISO 527-3 |
| Drop hammer impact | |||
| 23 µm | 180 | g | ISO 7765-1/A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：23 µm | 200 | g | ASTM D1922 |
| TD：23 µm | 360 | g | ASTM D1922 |
| Unstretched bonding | 100 | g | ASTM D4649 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 90.0 | ℃ | ISO 306/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，23 µm | 92 | ASTM D2457 | |
| Haze | |||
| 23 µm | 0.70 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 260 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |