ATTANE™ NG 4701G

About
ATTANE™ NG 4701G Polyethylene Resin is a great abuse resistance copolymer offering extremely high impact strength, combined with good tear and exceptional optics. It has the added benefit of being easy to process (low melt temperature, low extruder amps and low screen pack backpressure) which translates into quality film rolls due to its bubble stability. Main Characteristics: Ultra low density ethylene/octene copolymer High performance film applications Complies with: U.S. FDA 21 CFR 177.1520(c)3.2a. Canadian HPFB No Objection Consult the regulations for complete details.&&

About

ATTANE™ NG 4701G Polyethylene Resin is a great abuse resistance copolymer offering extremely high impact strength, combined with good tear and exceptional optics. It has the added benefit of being easy to process (low melt temperature, low extruder amps and low screen pack backpressure) which translates into quality film rolls due to its bubble stability. Main Characteristics: Ultra low density ethylene/octene copolymer High performance film applications Complies with: U.S. FDA 21 CFR 177.1520(c)3.2a. Canadian HPFB No Objection Consult the regulations for complete details.&&

Product Description
Supplier	DOW
Generic	VLDPE
Material Status	Commercial: Negative
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.912	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	0.80	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	25	µm
Membrane puncture strength	6.21	J	Internal Method
Membrane puncture force	71.2	N	Internal Method
Membrane puncture resistance	33.1	J/cm³	Internal Method
Membrane strength			ASTM D882
MD	72.8	J/cm³	ASTM D882
TD	70.3	J/cm³	ASTM D882
Secant modulus			ASTM D882
1% secant, MD	141	MPa	ASTM D882
2% secant, MD	124	MPa	ASTM D882
1% secant, TD	148	MPa	ASTM D882
2% secant, TD	131	MPa	ASTM D882
tensile strength			ASTM D882
MD, yield	8.96	MPa	ASTM D882
TD, yield	8.62	MPa	ASTM D882
MD, fracture	41.4	MPa	ASTM D882
TD, fracture	37.2	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture	400	%	ASTM D882
TD, fracture	450	%	ASTM D882
Drop hammer impact	380	g	ASTM D1709B
Elmandorf tear strength			ASTM D1922
MD	250	g	ASTM D1922
TD	600	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	99.0	℃	ASTM D1525
Melting temperature
DSC	101	℃	ISO 3146

optical performance	Nominal value	Unit	Test method
gloss
45°	49		ASTM D2457
Haze	11	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.