| About |
|---|
| Features Non Reinforced/Filled Excellent Cleanness (Low Outgassing, Low Level Impurities)&& |
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Material Status | Commercial: Negative |
| Features | Low odor,High purity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Molding shrinkage | Internal Method | ||
| MD | 0.7 | % | Internal Method |
| TD | 0.8 | % | Internal Method |
| Melt Flow Rate | |||
| 400℃，1.05 kg | 8 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | 90 | MPa | ASTM D638 |
| Tensile Strain | |||
| Broken BRK | 90 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 140 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Unnotched Impact strength of cantilever beam | 88 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa | 230 | ℃ | ASTM D648 |
| Coeff. of linear thermal expansion | ASTM D696 | ||
| MD | 5.5 | ×10-5/℃ | ASTM D696 |
| TD | 5.5 | ×10-5/℃ | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 200 | ℃ | |
| Drying Time | >5 | hr | |
| Rear Temperature Zone 1 | 390-400 | ℃ | |
| Middle Temperature Zone 2 | 400-410 | ℃ | |
| Front Temperature Zone 3 | 400-410 | ℃ | |
| Nozzle temperature | 400-410 | ℃ | |
| Mold Temperature | 180-200 | ℃ | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |