| About |
|---|
| Avantra® 8530B is an ignition resistant grade of high impact polystyrene with exceptional moldability. It is free of polybrominated diphenylethers and meets UL94V-0 (@ 0.062″/1.5 mm min.) rating. It gives exceptional moldability while maintaining good mechanical and heat resistance properties. Applications Avantra® 8530B is best suited for gas-assist molding applications of large size electronic/electrical enclosures.&& |
| Product Description | |
|---|---|
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Flame Characteristics,Heat Resistance, Good,V-0,5VA,5VB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 13 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.30 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| saturated | < 0.15 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% | < 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 19.0 | MPa | ASTM D638 |
| yield | 23.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 55 | % | ASTM D638 |
| Bending modulus | 2070 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 120 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 75.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 95.0 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, all colors | V-0 | UL 94 | |
| 2.60 mm, natural color | 5VB | UL 94 | |
| 3.00 mm, black | 5VB | UL 94 | |
| 5.50 mm, all colors | 5VA | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 240 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |