| About |
|---|
| AvaSpire® AV-481 is an unreinforced PAEK (polyaryletherketone) that offers improved ductility and impact strength relative to PEEK while offering similar or superior melt processability to high melt flow PEEK that is available on the market. Chemical resistance and environmental stress cracking resistance of AV-481 are also on par with that of unreinforced PEEK. This product has been specifically formulated for applications requiring an excellent balance of chemical resistance and mechanical toughness along with very high melt flow characteristics to allow filling of very thin and long flow length parts like cable ties. The heat resistance of this grade is also quite high with a heat distortion temperature in excess of 200°C and very good long term oxidative stability at elevated temperatures. This combination of properties makes AV-481 well-suited for applications in automotive, aerospace, electrical/electronics, and other industrial uses. AvaSpire® AV-481 is an injection molding grade and can be easily processed by typical injection molding methods using standard equipment. The material is available in two standard colors: beige (AV-481 BG15) and black (AV-481 BK95). Because the material is naturally lighter in color than typical PEEK resin, AV-481 provides greater versatility in its ability to be colored. Beige: AV-481 BG 15 Black: AV-481 BK 95&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PAEK |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good Dimensional Stability,High liquidity,Ductility,High Heat Resistance,Fatigue resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 3200 | MPa | ASTM D638 |
| tensile strength | 97.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 6.3 | % | ASTM D638 |
| fracture | > 15 | % | ASTM D638 |
| Bending modulus | 3300 | MPa | ASTM D790 |
| bending strength | 141 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 64 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 无断裂 | ASTM D4812 | |
| Dart impact equipped with measuring instruments | 78.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 3.2 mm | 208 | ℃ | ASTM D648 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | ASTM D792 | ||
| — | 1.33 | g/cm³ | ASTM D792 |
| — | 1.34 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 55 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| Apparent viscosity of melt | |||
| 400℃，1000 sec^-1 | 170 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 355 | °C | |
| Barrel middle temperature | 365 | °C | |
| Barrel front temperature | 370 | °C | |
| Nozzle temperature | 375 | °C | |
| Mold temperature | 175 to 205 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. AvaSpire® AV-481 BK 95 |
| 3. AvaSpire® AV-481 BG 15 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |