| AvaSpire® AV-621 GF30 is a 30% glass fiber reinforced version of AvaSpire® AV-621. This formulation offers better dimensional stability and lower warpage than 30% glass reinforced PEEK. This resin retains most of the desirable ultra-performance attributes of glass reinforced PEEK, including chemical resistance, fatigue resistance and long term thermal oxidative stability, but the heat deflection temperature is lower than 30% GF PEEK. The material’s excellent balance of properties makes it well suited for demanding applications across a broad range of industries including healthcare, transportation, electronics, oil and gas, and chemical processing. Beige: AV-621 GF30 BG 20 Black: AV-621 GF30 BK 95&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PAEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Fatigue resistance,Solvent resistance,V-1,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| — | 120 | J/m | ASTM D256 |
| — | 14 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | |||
| — | 1000 | J/m | ASTM D4812 |
| — | 70 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 217 | ℃ | ASTM D648 |
| Glass transition temperature | 158 | ℃ | ASTM D3418 |
| Melting peak temperature | 340 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD：-50~50℃ | 1.7E-5 | 1/℃ | ASTM E831 |
| specific heat | DSC | ||
| 50℃ | 1290 | J/kg/℃ | DSC |
| 200℃ | 1660 | J/kg/℃ | DSC |
| Thermal conductivity coefficient | 0.28 | W/m/K | ASTM E1530 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.9E+17 | ohms | ASTM D257 |
| Volume resistivity | 2.1E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3 mm | 15 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.52 | ASTM D150 | |
| 1 kHz | 3.53 | ASTM D150 | |
| 1 MHz | 3.48 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 1.0E-3 | ASTM D150 | |
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 5.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-1 | UL 94 | |
| 1.60 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 101 | ASTM D785 | |
| Tensile modulus | |||
| — | 9900 | MPa | ASTM D638 |
| — | 10600 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 158 | MPa | ISO 527-2/1A/5 |
| — | 147 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.2 | % | ASTM D638 |
| fracture | 3.2 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| — | 9400 | MPa | ASTM D790 |
| — | 9800 | MPa | ISO 178 |
| bending strength | |||
| — | 237 | MPa | ASTM D790 |
| — | 236 | MPa | ISO 178 |
| compressive strength | 159 | MPa | ASTM D695 |
| shear strength | 84.5 | MPa | ASTM D732 |
| Poisson’s ratio | 0.43 | ASTM E132 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：3.2 mm | 0.10 to 0.30 | % | ASTM D955 |
| TD：3.2 mm | 0.90 to 1.1 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.20 | % | ASTM D570 |
| Apparent viscosity of melt | |||
| 400℃，1000 sec^-1 | 650 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 366 | °C | |
| Barrel middle temperature | 371 | °C | |
| Barrel front temperature | 377 | °C | |
| Nozzle temperature | 382 | °C | |
| Processing (melt) temperature | 366 to 388 | °C | |
| Mold temperature | 149 to 177 | °C | |
| Notes |
|---|
| 1. Only AvaSpire® AV-621 BG20 is ISO 10993 certified |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 5″ x 0.5″ x 0.125″ bars |
| 4. 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |