| AvaSpire® AV-651 GF30 is a 30% glass fiber reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide higher mechanical strength and stiffness than unfilled AV-651 resin. This resin offers chemical resistance nearly equivalent to glass fiber-reinforced PEEK in most chemicals, with a lower heat deflection temperature. These properties make it well suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses. Beige: AvaSpire® AV-651 GF30 BG 20 Black: AvaSpire® AV-651 GF30 BK 95&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PAEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Good disinfection,Steam sterilized,Gamma radiation,E-beam disinfection,Biocompatible,Flame Characteristics,High pressure disinfection,High Heat Resistance,Radioactive,Fatigue resistance,Radiation disinfection,Solvent resistance,Resistance to the steam,Ethylene oxide disinfection,Heat sterilization,V-1,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| — | 110 | J/m | ASTM D256 |
| — | 12 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | |||
| — | 960 | J/m | ASTM D4812 |
| — | 64 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 213 | ℃ | ASTM D648 |
| Glass transition temperature | 158 | ℃ | ASTM D3418 |
| Melting peak temperature | 345 | ℃ | ASTM D3418 |
| Linear coefficient of thermal expansion | |||
| MD：-50~50℃ | 1.7E-5 | 1/℃ | ASTM E831 |
| specific heat | DSC | ||
| 50℃ | 1270 | J/kg/℃ | DSC |
| 200℃ | 1650 | J/kg/℃ | DSC |
| Thermal conductivity coefficient | 0.30 | W/m/K | ASTM E1530 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.9E+17 | ohms | ASTM D257 |
| Volume resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 3 mm | 17 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 3.61 | ASTM D150 | |
| 1 kHz | 3.63 | ASTM D150 | |
| 1 MHz | 3.58 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 60 Hz | 2.0E-3 | ASTM D150 | |
| 1 kHz | 0.0 | ASTM D150 | |
| 1 MHz | 4.0E-3 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-1 | UL 94 | |
| 1.60 mm | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 101 | ASTM D785 | |
| Tensile modulus | |||
| — | 9900 | MPa | ASTM D638 |
| — | 10400 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| Yield, 5 mm | 162 | MPa | ISO 527-2/1A/5 |
| — | 156 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.9 | % | ASTM D638 |
| fracture | 2.9 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| — | 9400 | MPa | ASTM D790 |
| — | 9700 | MPa | ISO 178 |
| bending strength | |||
| — | 234 | MPa | ASTM D790 |
| — | 228 | MPa | ISO 178 |
| compressive strength | 168 | MPa | ASTM D695 |
| shear strength | 82.6 | MPa | ASTM D732 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 9.0 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：3.2 mm | 0.20 to 0.40 | % | ASTM D955 |
| TD：3.2 mm | 1.3 to 1.5 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.20 | % | ASTM D570 |
| Apparent viscosity of melt | |||
| 400℃，1000 sec^-1 | 410 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 365 | °C | |
| Barrel middle temperature | 371 | °C | |
| Barrel front temperature | 377 | °C | |
| Nozzle temperature | 382 | °C | |
| Processing (melt) temperature | 366 to 388 | °C | |
| Mold temperature | 160 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 5″ x 0.5″ x 0.125″ bars |
| 3. 0,20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |