| About |
|---|
| AvaSpire® AV-848 CF30 is a 30% carbon fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of PEEK. These include improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 CF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire® AV-848 CF30 can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PAEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Fatigue resistance,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 3.5 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.0 to 0.20 | % | ASTM D955 |
| TD | 0.40 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 18800 | MPa | ASTM D638 |
| tensile strength | 176 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.5 | % | ASTM D638 |
| Bending modulus | 16500 | MPa | ASTM D790 |
| bending strength | 259 | MPa | ASTM D790 |
| compressive strength | 145 | MPa | ASTM D695 |
| shear strength | 95.0 | MPa | ASTM D732 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 43 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 530 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 257 | ℃ | ASTM D648 |
| Glass transition temperature | 158 | ℃ | DSC |
| Melting peak temperature | 340 | ℃ | ASTM D3418 |
| Thermal conductivity coefficient | 0.037 | W/m/K | ASTM E1530 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 366 | °C | |
| Barrel middle temperature | 371 | °C | |
| Barrel front temperature | 377 | °C | |
| Nozzle temperature | 382 | °C | |
| Processing (melt) temperature | 382 to 404 | °C | |
| Mold temperature | 166 to 193 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |