| AVP™ RY633CP是一种聚酰胺6（尼龙6）产品,含有的填充物为33% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在北美洲有供货。 主要特性为:热稳定剂。&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.30 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength（Ultimate，3.18 mm） | 138 | MPa | ASTM D638 |
| Bending modulus | |||
| 3.18 mm, 50.80 mm span | 6210 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 69 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.35 mm | 210 | ℃ | ASTM D648 |
| Melting temperature | 216 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 2.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended injection volume | 40 to 80 | % | |
| Barrel rear temperature | 227 to 260 | °C | |
| Barrel middle temperature | 243 to 277 | °C | |
| Barrel front temperature | 260 to 293 | °C | |
| Nozzle temperature | 260 to 293 | °C | |
| Processing (melt) temperature | 260 to 293 | °C | |
| Mold temperature | 66 to 110 | °C | |
| Back pressure | 0.172 to 1.03 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |