| AVP™ RYY13UVCP是一种聚酰胺66（尼龙66）产品,含有的填充物为13% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在北美洲有供货。 特性包括: 热稳定剂 紫外线稳定 良好的抗紫外线能力&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Heat Stabilized |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength（Ultimate，3.18 mm） | 103 | MPa | ASTM D638 |
| Bending modulus | |||
| 3.18 mm, 50.80 mm span | 4480 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 37 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.35 mm | 232 | ℃ | ASTM D648 |
| Melting temperature | 249 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 2.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended injection volume | 40 to 80 | % | |
| Barrel rear temperature | 249 to 282 | °C | |
| Barrel middle temperature | 260 to 288 | °C | |
| Barrel front temperature | 271 to 304 | °C | |
| Nozzle temperature | 271 to 304 | °C | |
| Processing (melt) temperature | 271 to 304 | °C | |
| Mold temperature | 66 to 110 | °C | |
| Back pressure | 0.172 to 1.03 | MPa | |
| Screw speed | 50 to 150 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |