| About |
|---|
| AVP™ TLL12CU是一种聚碳酸酯（PC）产品,。 它可以通过注射成型进行加工,在北美洲有供货。 AVP™ TLL12CU的应用领域包括电气/电子应用、电气用具 和 汽车行业。 特性包括: 环保/绿色 高强度 坚硬 良好的抗紫外线能力 良好的韧性&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good flexibility,Good liquidity |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 129 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2410 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 58.6 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 120 | % | ASTM D638 |
| Bending modulus | 2410 | MPa | ASTM D790 |
| bending strength | |||
| yield | 89.6 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-grade, 3.18 mm | 120 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 4.0 | hr | |
| Drying time, maximum | 16 | hr | |
| Barrel rear temperature | 266 to 282 | °C | |
| Barrel middle temperature | 271 to 282 | °C | |
| Barrel front temperature | 277 to 293 | °C | |
| Nozzle temperature | 271 to 293 | °C | |
| Processing (melt) temperature | 288 to 316 | °C | |
| Mold temperature | 77 to 99 | °C | |
| Back pressure | 0.345 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |