AXELERON™ CS K-3364 NT CPD

About
AXELERON™ CS K-3364 NT CPD is a high-molecular weight, high-density polyethylene insulation compound (“CPD”) specifically formulated to provide excellent oxidative stability, toughness, and abrasion resistance. It provides superior long term aging performance, while providing excellent environmental and thermal stress-cracking resistance. In addition, AXELERON™ CS K-3364 NT CPD provides excellent processability for high-speed wire insulating extrusion processes. AXELERON™ CS K-3364 NT CPD provides good performance for telephone insulation applications, primarily cable designs for aerial environments. AXELERON™ CS K-3364 NT CPD is optimized to meet major international age testing standards and specifications for both solid and foam/skin insulation use. Specifications AXELERON™ CS K-3364 NT CPD meets the following raw material specifications: ASTM D 1248 Type III Category A-4, Grade E8 and E9 Federal LP-390 C, II-H, Grades 1 and 2, Category 4 ISO 1872-PE, KHKN,45-D006 Telephone wire insulated with AXELERON™ CS K-3364 NT CPD, using sound commercial extrusion practices, should meet the following cable specifications: ICEA S-84-608 EN-50290-2-23 IEC 60708 DIN VDE 0819-103 BS 6234 type H03 NF C 32-060&&

About

AXELERON™ CS K-3364 NT CPD is a high-molecular weight, high-density polyethylene insulation compound (“CPD”) specifically formulated to provide excellent oxidative stability, toughness, and abrasion resistance. It provides superior long term aging performance, while providing excellent environmental and thermal stress-cracking resistance. In addition, AXELERON™ CS K-3364 NT CPD provides excellent processability for high-speed wire insulating extrusion processes. AXELERON™ CS K-3364 NT CPD provides good performance for telephone insulation applications, primarily cable designs for aerial environments. AXELERON™ CS K-3364 NT CPD is optimized to meet major international age testing standards and specifications for both solid and foam/skin insulation use. Specifications AXELERON™ CS K-3364 NT CPD meets the following raw material specifications: ASTM D 1248 Type III Category A-4, Grade E8 and E9 Federal LP-390 C, II-H, Grades 1 and 2, Category 4 ISO 1872-PE, KHKN,45-D006 Telephone wire insulated with AXELERON™ CS K-3364 NT CPD, using sound commercial extrusion practices, should meet the following cable specifications: ICEA S-84-608 EN-50290-2-23 IEC 60708 DIN VDE 0819-103 BS 6234 type H03 NF C 32-060&&

Product Description
Supplier	DOW
Generic	HDPE
Material Status	Commercial: Active
Availabilitys	Europe,Latin America,Asia Pacific,North America,Africa & Middle East

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.947	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	0.75	g/10min	ASTM D1238
ESCR(Environmental Stress Cracking Resistance)
100 ℃, 100% non-ionic detergent, F0	> 48.0	hr	ASTM D1693

MECHANICAL	Nominal value	Unit	Test method
Tensile Strength	23.4	MPa	ASTM D638
Tensile Strain
Broken BRK	500	%	ASTM D638

Aging property	Nominal value	Unit	Test method
Retention of Tensile Strength
48 hrs，100℃	90	%	ASTM D638
Retention of Tensile Strength
48 hrs，100℃	90	%	ASTM D638

THERMAL	Nominal value	Unit	Test method
Brittle Temperature	-76.0	℃	ASTM D746
Hot deformation temperature HDT
F0	> 96	hr	ASTM D2951

ELECTRICAL	Nominal value	Unit	Test method
Volume Resistance
23℃	> 1.0E+15	ohms·cm	ASTM D257
Dielectric Constant
1 MHz	2.32		ASTM D1531
Dissipation Factor
1 MHz	6.0E-5		ASTM D1531

Process Conditions
Extrusion Molded	Nominal value	Unit	Test method
Melt Temperature	218 to 260	°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. F0
3. After 14 days Water Immersion at 23°C (73°F)
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.