| 12770 is a flexible extrusion PVC compound for CATV jacketing applications requiring sunlight resistance and excellent low temperature properties.&& |
| Product Description | |
|---|---|
| Supplier | Axiall Corporation |
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Antifreeze |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 to 1.36 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 10 seconds | 74 to 80 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| — | 15.2 | MPa | ASTM D638 |
| 100% strain | 7.58 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 350 | % | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -44.0 | ℃ | ASTM D746 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in ultimate elongation in air | |||
| 100℃，240 hr | -11 | % | UL 1581 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 23 | % | ASTM D2863 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Stock Temperature | 182 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 30 mil slab |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |