| About |
|---|
| HR-5009 is a rigid injection molding PVC compound for interior fittings. This compound is designed for hot sprue/runner molds, large parts and multi-cavity molds. The HR-5009 compound is characterized by excellent process ability, which includes color hold, regrind and surface appearance. HR-5009 is NSF listed under Standard 14 and Standard 61 for both potable water and DWV applications.&& |
| Product Description | |
|---|---|
| Supplier | Axiall Corporation |
| Generic | PVC，刚硬 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 to 1.41 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.20 to 0.30 | % | ASTM D955 |
| PVC unit classification | 12454 | ASTM D1784 | |
| Flow Ratio（199 to 204℃） | 170 | Internal Method | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2830 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 50.3 | MPa | ASTM D638 |
| Bending modulus | 2900 | MPa | ASTM D790 |
| bending strength | 89.6 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃，3.2mm | 37 | J/m | ASTM D256 |
| 23℃，3.2mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 71.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 75.0 | ℃ | ASTM D648 |
| Melting temperature | 199 to 204 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | 38 | % | ASTM D2863 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Distance/Wall Thickness |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |