| AXIALL’s Georgia Gulf NR-5009 is a high flow rigid, fitting-grade vinyl compound designed for small gated, thin walled parts. The compound is characterized by excellent processability, which includes color hold, regrind stability, and surface appearance. NR-5009 is NSF listed for DMV and pressure fittings applications.&& |
| Product Description | |
|---|---|
| Supplier | Axiall Corporation |
| Generic | PVC，刚硬 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,High liquidity,Good color stability,V-0 |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.20 to 0.30 | % | ASTM D955 |
| PVC unit classification | 12454-B | ASTM D1784 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃，3.2mm | 37 | J/m | ASTM D256 |
| 23℃，3.2mm | 59 | J/m | ASTM D256 |
| Drop hammer impact | |||
| 23℃ | 36.2 | J | ASTM D3029 |
| Falling impact resistance | |||
| 23℃ | 116 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 75.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 71.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | 38 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| Tensile modulus | 2830 | MPa | ASTM D638 |
| tensile strength | 50.3 | MPa | ASTM D638 |
| Bending modulus | 2900 | MPa | ASTM D790 |
| bending strength | 89.6 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 66 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 6.0 | hr | |
| Recommended injection volume | 35 to 75 | % | |
| Proposed maximum recycled material ratio | 50 | % | |
| Barrel rear temperature | 163 | °C | |
| Barrel middle temperature | 174 to 191 | °C | |
| Barrel front temperature | 182 to 193 | °C | |
| Nozzle temperature | 177 to 193 | °C | |
| Processing (melt) temperature | 202 to 210 | °C | |
| Mold temperature | 16 to 49 | °C | |
| Injection pressure | 82.7 to 138 | MPa | |
| Hold pressure | 48.3 to 82.7 | MPa | |
| Back pressure | 0.345 to 1.38 | MPa | |
| Screw speed | 25 to 80 | rpm | |
| Clamping force | 3.4 | kN/cm² | |
| Screw length to diameter ratio | 16.0:1.0 to 24.0:1.0 | ||
| Screw compression ratio | 1.5:1.0 to 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |