| SP-5034 is a rigid vinyl injection molding PVC compound for fittings and parts of similar configuration where maximum burst strength is required. SP-5034 is ideally suited for large diameter fittings. SP-5034 is listed with NSF under Standard 14, and meets Standard 61 health effects requirements.&& |
| Product Description | |
|---|---|
| Supplier | Axiall Corporation |
| Generic | PVC，刚硬 |
| Material Status | Commercial: Active |
| Features | Good Rigidity |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.34 to 1.38 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.20 to 0.40 | % | ASTM D955 |
| PVC unit classification | 12454-B | ASTM D1784 | |
| Flow Ratio（199 to 204℃） | 120 | Internal Method | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃，3.2mm | 37 | J/m | ASTM D256 |
| 23℃，3.2mm | 80 | J/m | ASTM D256 |
| Resistance to drop impact | |||
| 23℃ | 114 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 70.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 74.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 38 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2760 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 48.3 | MPa | ASTM D638 |
| Bending modulus | 3100 | MPa | ASTM D790 |
| bending strength | 82.7 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Distance/Wall Thickness |
| 3. Procedure A, C 1/2″ R Tup |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |