| BAAF UHMW-PE 3000 NC is a High Density (UHMW) Polyethylene material. It is available in Asia Pacific or Europe.&& |
| Product Description | |
|---|---|
| Generic | Ultra-high molecular weight polyethylene |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.935 to 0.940 | g/cm³ | Internal Method |
| Apparent density | Internal Method | ||
| — | > 0.35 | g/cm³ | Internal Method |
| — | > 0.38 | g/cm³ | Internal Method |
| molecular weight | 3000000 to 4000000 | Internal Method | |
| Volatiles | < 0.15 | wt% | Internal Method |
| Particle size | > 98.0 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | Internal Method | ||
| fracture | > 35.0 | MPa | Internal Method |
| fracture | > 32.0 | MPa | Internal Method |
| Tensile strain | Internal Method | ||
| fracture | 300 | % | Internal Method |
| fracture | 250 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | Internal Method | ||
| — | > 100 | kJ/m² | Internal Method |
| — | > 70 | kJ/m² | Internal Method |
| Notched impact strength of cantilever beam | 无断裂 | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 80.0 | ℃ | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. M-1 B |
| 3. M-1 A |
| 4. through 20 mesh sieve |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |