| About |
|---|
| 20% glass fiber reinforced injection moulding grade with high resistance to heat, good strength and electrical properties&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Good Electrical Properties,High Heat Resistance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，10 kg | 11.0 | cm³/10min | ISO 1133 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.15 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 6000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 90.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 25 | kJ/m² | ISO 179/1eU |
| 23℃ | 25 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 6.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 170 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 160 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 170 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | DIN 53752 | ||
| MD | 3.0E-5 | 1/℃ | DIN 53752 |
| TD | 7.0E-5 | 1/℃ | DIN 53752 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | IEC 60243-1 | ||
| 0.8 mm in oil | 30 | kV/mm | IEC 60243-1 |
| 1.6 mm in oil | 26 | kV/mm | IEC 60243-1 |
| 3.2 mm in oil | 16 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 2.60 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 6.0E-3 | IEC 60250 | |
| 60 Hz | 6.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 290 to 330 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Test Specimen accordng to ISO 3167, Type A |
| 3. 80x10x4 mm |
| 4. 110x10x4 mm |
| 5. Compound for moulding |
| 6. >10x10x4 mm |
| 7. 80x80x1 mm |
| 8. 125x13x1.5 mm |
| 9. 125x13x3.0 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |