| About |
|---|
| 30% glasfibres filled tribological injection moulding grade; Low friction and wear at high high service temperature&& |
| Product Description | |
|---|---|
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Heat Stabilized,V-0 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.62 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 11500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 160 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.7 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 4.0 mm | 270 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 295 | ℃ | ISO 3146 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.75 mm | 960 | ℃ | IEC 60695-2-12 |
| 1.6 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.75 mm | 960 | ℃ | IEC 60695-2-13 |
| 1.6 mm | 960 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 300 to 340 | °C | |
| Mold temperature | 140 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80x10x4 mm |
| 3. 110x10x4 mm |
| 4. Compound for molding, 10k/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |