| About |
|---|
| BPP035A, a composite of PP and bamboo fiber.BFC environmental plastic, with natural fiber, possesses the functions of anti-biosis and deodorization that can keep your health.what’s more ,this material keeps a low shrinkage ,which give the products a soothing and fine looking surface.&& |
| Product Description | |
|---|---|
| Supplier | Bamtac |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Low contractility |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 to 1.07 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 9.0 to 13 | g/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.70 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | > 4.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 105 | ℃ | ISO 75-2/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 to 75 | ||
| Tensile modulus | > 3500 | MPa | ISO 527-2 |
| tensile strength | > 25.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 2.0 | % | ISO 527-2 |
| Bending modulus | > 2500 | MPa | ISO 178 |
| bending strength | > 50.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |