| Barex 210 Extrusion Grade resin is an impact modified acrylonitrile-methyl acrylate copolymer with excellent gas barrier and a wide range of chemical resistance properties. It can easily be used for producing high barrier packaging by film and sheet extrusion, thermoforming, and extrusion blow molding.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | 丙烯腈+丙烯酸甲酯 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Food contact compliance,Block resin,Solvent resistance |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Apparent density | 0.66 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | 3.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ASTM D955 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen permeability | |||
| 23℃，100% RH | 0.31 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water vapor transmittance | 2.0 | g·mm/m²/atm/24 hr | ASTM F1249 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 270 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 76.7 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 68.9 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：20~80℃ | 6.7E-5 | 1/℃ | ASTM D696 |
| specific heat | |||
| 20℃ | 1340 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | 0.25 | W/m/K | ASTM C177 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60°，254 µm | 120 | ASTM D2457 | |
| Transmittance | |||
| 254 µm | 92.5 | % | ASTM D1003 |
| Haze | |||
| 254 µm | 2.7 | % | ASTM D1003 |
| Yellowness index | |||
| 0.254 mm | 2.5 | YI | ASTM D1925 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 60 | ASTM D785 | |
| tensile strength | |||
| yield | 65.5 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 3.0 | % | ASTM D638 |
| Bending modulus | 3380 | MPa | ASTM D790 |
| bending strength | |||
| yield | 96.5 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |