| About |
|---|
| (PC+ABS) blend; flame-retardant; extrusion grade; Vicat/B120 = 122 °C; UL 94 V-0 (1.5 mm) and V-1 (0.75 mm) (internal test); for pipe- and corrugated pipe extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-1,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 23℃ | 2500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 60.0 | MPa | ISO 527-2/50 |
| Yield, 23 ℃ | 65.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 50 | % | ISO 527-2/50 |
| Yield, 23 ℃ | 5.0 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30℃ | 10 | kJ/m² | ISO 180-A |
| 23℃ | 40 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 104 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 120 | ℃ | ISO 306 |
| B120 | 122 | ℃ | ISO 306/B120 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm, Bayer test | V-1 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melt Volume Rate | |||
| 260℃，5 kg | 22.0 | cm³/10min | ISO 1133 |
| Apparent viscosity of melt | |||
| 260℃ | 410 | Pa·s | ISO 11443-A |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |