| (PC+ABS)-Blend; easy flowing; Vicat/B 120 temperature = 103°C; UL recognition 94 V-0 at 1.5 mm; no juicing; good light stability |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good liquidity,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 23℃ | 2650 | MPa | ISO 527-1-2 |
| Tensile stress (yield, 23 ° C) | 64.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 3.9 | % | ISO 527-2/50 |
| Nominal tensile fracture strain (23 ° C) | 40 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 30 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 85.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 103 | ℃ | ISO 306/B120 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 23℃，100 Hz | 3.00 | ||
| 23℃，1 MHz | 2.90 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| Extreme oxygen index | 34 | % | ISO 4589-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | |||
| 23℃ | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 240℃，5 kg | 20.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.40 to 0.60 | % | |
| MD | 0.40 to 0.60 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.40 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | |
| Melt viscosity (240 ° C) | 150 | Pa·s | ISO 11443-A |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying temperature – Dry Air Dryer | 80 | °C | |
| Drying time – Dry Air Dryer | 4.0 | hr | |
| Recommended maximum moisture content | < 0.020 | % | |
| Suggested injection volume | 30 to 70 | % | |
| Temperature at the rear of the barrel | 220 to 230 | °C | |
| Temperature in the middle of the barrel | 225 to 235 | °C | |
| Front temperature of material barrel | 230 to 240 | °C | |
| Nozzle temperature | 255 to 265 | °C | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Back pressure | 5.00 to 15.0 | MPa | |
| Exhaust hole depth | 0.025 to 0.075 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |