| About |
|---|
| (PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 108°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; optimized processability; good light stability&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good liquidity,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：2.0 mm | 0.60 | % | ISO 294-4 |
| TD：2.0 mm | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | ISO 62 |
| 23℃，50% RH | 0.20 | % | ISO 62 |
| Melt Flow Rate | |||
| 240℃，5.0kg | 25 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 60 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 50 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 2700 | MPa | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 90 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 106 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 7.6E-5 | 1/℃ | ISO 11359-2 |
| TD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+16 | Ω.cm | IEC 60093 |
| Surface resistance | 1.0E+16 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 35 | KV/mm | IEC 60243-1 | |
| Dielectric constant | |||
| 23℃ | 3.1 | 1 MHz | IEC 60250 |
| Dissipation factor | |||
| 23℃ | 7.0E-3 | 1 MHz | IEC 60250 |
| Compared to the leakage tracing index | 350 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | UL 94 | ||
| 1.00mm | UL 94 | ||
| 1.50mm | V-0 | UL 94 | |
| 2.20mm | V-0，5VB | UL 94 | |
| 3.00mm | V-0，5VA | UL 94 | |
| Igniting temperature of the hot wire | |||
| 1 mm | 850 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 850 | ℃ | IEC 60695-2-12 |
| 2.2 mm | 850 | ℃ | IEC 60695-2-12 |
| 3 mm | 850 | ℃ | IEC 60695-2-12 |
| Relative temperature of heating wire | |||
| 1.00mm | 960 | ℃ | IEC 60695-2-13 |
| 1.50mm | 960 | ℃ | IEC 60695-2-13 |
| 2.20mm | 960 | ℃ | IEC 60695-2-13 |
| 3.00mm | 960 | ℃ | IEC 60695-2-13 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 35 | kJ/m² | ISO 180-1A |
| -30℃ | 10 | kJ/m² | ISO 180-1A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mold Temperature: 176°F, Melt Temperature: 500°F |
| 3. 2x8mm |
| 4. 150x105x3mm,, MT 80°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |