| About |
|---|
| (PC+ABS)-Blend; 15% glass fibre reinforced; flame retardant; Vicat/B 120 temperature = 100°C; UL recognition 94V-1 at 1.2 mm and V-0 at 1.5 mm&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0,V-1 |
| Availabilitys | Latin America,Europe,Asia Pacific,North America,Africa & Middle East |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 23℃ | 5300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 95.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.0 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 30 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 98.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 92.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 98.0 | ℃ | ISO 306 |
| B120 | 100 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~55℃ | 4.0E-5 | 1/℃ | |
| TD：23~55℃ | 7.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | |||
| 23℃ | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 23 ℃，1 mm | 35 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 23℃，100 Hz | 3.20 | ||
| 23℃，1 MHz | 3.10 | ||
| Dissipation factor | IEC 60250 | ||
| 23℃，100 Hz | 5.0E-3 | ||
| 23℃，1 MHz | 7.0E-3 | ||
| Compared to the leakage tracing index | |||
| Solution A | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.20 mm | V-1 | ||
| 1.50 mm | V-0 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 23.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 2577 | ||
| TD：240℃，3.0 mm | 0.30 to 0.50 | % | |
| MD：240℃，3.0 mm | 0.20 to 0.40 | % | |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.40 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.10 | % | |
| Apparent viscosity of melt | |||
| 260℃ | 185 | Pa·s | ISO 11443-A |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Melt Temperature | 290 – 330 | ℃ | |
| Standard melt temperature | 310 | ℃ | |
| Temperature of the feeding section of the material pipe | 260 – 270 | ℃ | |
| Temperature of the middle section of the material pipe | 280 – 290 | ℃ | |
| Temperature of the front section of the material pipe | 290 – 300 | ℃ | |
| Nozzle temperature | 300 – 310 | ℃ | |
| Mold temperature | 80 – 120 | ℃ | |
| Maintaining pressure (actual maximum injection pressure) | 50 – 75 | % | |
| Melt back pressure | 50 – 150 | bar | |
| Screw speed | 0.05 – 0.2 | m/s | |
| Injection volume | 30 – 70 | % | |
| Dry explosion temperature in dry air | 120 | ℃ | |
| Dry explosion time in dry air | 2 – 3 | h | |
| Maximum moisture content | ≤0.02 | % | |
| Depth of exhaust groove | 0.025 – 0.075 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 150x105x3mm,, MT 80°C |
| 3. 1000s-1 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |