Baydur® 641 IBS (30 pcf)

About
Baydur 641 IBS is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system is supplied as two reactive liquid components and is typically used with a blowing paste purchased separately. Component A is a polymeric diphenylmethane diisocyanate (PMDI). Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. The blowing paste is Baydur PU-1731. The Baydur 641 IBS system is used in the industrial and medical equipment markets for applications requiring dimensional stability and excellent surface finish, such as, rollers for photographic and X-ray film processing equipment. As with any product, use of Baydur 641 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&&

About

Baydur 641 IBS is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system is supplied as two reactive liquid components and is typically used with a blowing paste purchased separately. Component A is a polymeric diphenylmethane diisocyanate (PMDI). Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. The blowing paste is Baydur PU-1731. The Baydur 641 IBS system is used in the industrial and medical equipment markets for applications requiring dimensional stability and excellent surface finish, such as, rollers for photographic and X-ray film processing equipment. As with any product, use of Baydur 641 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&&

Product Description
Supplier	Covestro
Generic	PUR+MDI
Material Status	Commercial: Active
Features	Good surface appearance,Good Dimensional Stability
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.479	g/cm³	ASTM D792
Shrinkage rate
MD：12.7 mm	0.30 to 0.50	%	ASTM D955

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength	9.0	kJ/m²	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore D, 12.70 mm	61		ASTM D2240
tensile strength
Fracture, 12.70 mm	9.65	MPa	ASTM D638
Tensile strain
Fracture, 12.70 mm	8.0	%	ASTM D638
Bending modulus
12.70 mm	483	MPa	ASTM D790
bending strength
12.70 mm	20.0	MPa	ASTM D790
compressive strength
12.7 mm	8.96	MPa	ASTM D695

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed, 12.7 mm	70.0	℃	ASTM D648
Thermosetting components
Component A	按重量计算的混合比: 110
Component B	按重量计算的混合比: 100

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.