| Baydur 645 is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. The system is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. The Baydur 645 system is used to produce foam cores for composite applications, such as water skis, agricultural and construction equipment, and various components for the transportation and marine markets. As with any product, use of the Baydur 645 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PUR+MDI |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.319 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 5.3 | kJ/m² | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw D, 6.35 mm | 37 | ASTM D2240 | |
| Shore D, 12.70 mm | 39 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| Fracture, 6.35 mm | 6.07 | MPa | ASTM D638 |
| Fracture, 12.70 mm | 6.21 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Fracture, 6.35 mm | 7.0 | % | ASTM D638 |
| Fracture, 12.70 mm | 9.0 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 6.35 mm | 303 | MPa | ASTM D790 |
| 12.70 mm | 248 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| 6.35 mm | 8.27 | MPa | ASTM D790 |
| 12.70 mm | 8.96 | MPa | ASTM D790 |
| compressive strength | ASTM D695 | ||
| 6.35 mm | 6.07 | MPa | ASTM D695 |
| 12.7 mm | 3.79 | MPa | ASTM D695 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.5 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |