| About |
|---|
| Bayflex XGT-16 Clear is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The formulated system is supplied as two liquid components: Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. Bayflex XGT-16 Clear system has a flexural modulus of 16,00 psi at room temperature. It is used in applications requiring excellent impact properties, such as bumpers for buses and other vehicles. As with any product, use of the Bayflex XGT-16 Clear system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PUR-脂肪族+MDI |
| Material Status | Commercial: Active |
| Features | High impact resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 , ASTM D1622 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.80 to 0.90 | % | Internal Method |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 16.5 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 3.18 mm | 250 | % | ASTM D412 |
| tear strength | |||
| 3.18 mm | 78.8 | kN/m | ASTM D624 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw A, 3.18 mm | 94 | ASTM D2240 | |
| Shaw D, 3.18 mm | 45 | ASTM D2240 | |
| Bending modulus | |||
| 3.18 mm | 110 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, H-18 wheels | 200 | mg | ASTM D1044 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD：3.2 mm | 1.4E-4 | 1/℃ | ASTM D696 |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 80, 按容量计算的混合比: 68 | ||
| Component B | 按重量计算的混合比: 100, 按容量计算的混合比: 100 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 1.05 Index |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |