| Bayflex XGT-80 is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two liquid components: Component A is a modified diphenylmethane diisocyanate (MDI), and Component B is a polyether polyol system. Note: The polyol component phase-separates upon standing and must be thoroughly mixed via mechanical means prior to use. The extended gel time of Bayflex XGT-80 gives equipment designers the flexibility to create large, complex parts that can be molded on existing injection machinery. The resin’s excellent surface quality and high impact resistance make it a candidate for agricultural equipment, heavy-duty trucks, specialty transportation, and marine applications.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PUR-脂肪族+MDI |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 , ASTM D1622 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.80 to 0.90 | % | Internal Method |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | |||
| 3.18 mm | 110 | kN/m | ASTM D624 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 640 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，3.18 mm | 5.42 | J | ASTM D3763 |
| 23℃，3.18 mm | 33.9 | J | ASTM D3763 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat Sag（4 in Overhang，121℃，3.18 mm） | 1.50 | cm | ASTM D3769 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw D, 3.18 mm | 65 | ASTM D2240 | |
| tensile strength | |||
| Fracture, 3.18 mm | 25.5 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.18 mm | 150 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| -30℃，3.18 mm | 1240 | MPa | ASTM D790 |
| 23℃，3.18 mm | 572 | MPa | ASTM D790 |
| 70℃，3.18 mm | 228 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 53.0 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：3.2 mm | 1.1E-4 | 1/℃ | ASTM D696 |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 140, 按容量计算的混合比: 120 | ||
| Component B | 按重量计算的混合比: 100, 按容量计算的混合比: 100 | ||
| Storage period | |||
| 32℃ | 26 | wk | |
| stripping time | 1.5 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 7.33 ft/sec |
| 4. 1.05 Index |
| 5. 0.125 in |
| 6. 1 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |