Baypreg® F (Glass Mat)

About
Baypreg F system is a two component polyurethane system used in compression molding of natural fiber mats alone, or fiber-reinforced sandwich panels to produce a variety of automotive parts. Some identified applications include door panels, sunshades, spare tire covers, load floors, etc. The Baypreg F system provides lightweight alternatives to ABS, PP, SMC, and wood products while demonstrating very high flexural stiffness and excellent thermal properties. Baypreg F system offers very diverse properties over a wide range of part thicknesses and densities while still providing cost effective substrate parts when combined with reinforcing materials. As with any product, use of the Baypreg F system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&&

About

Baypreg F system is a two component polyurethane system used in compression molding of natural fiber mats alone, or fiber-reinforced sandwich panels to produce a variety of automotive parts. Some identified applications include door panels, sunshades, spare tire covers, load floors, etc. The Baypreg F system provides lightweight alternatives to ABS, PP, SMC, and wood products while demonstrating very high flexural stiffness and excellent thermal properties. Baypreg F system offers very diverse properties over a wide range of part thicknesses and densities while still providing cost effective substrate parts when combined with reinforcing materials. As with any product, use of the Baypreg F system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&&

Product Description
Supplier	Covestro
Generic	PUR+MDI
Material Status	Commercial: Active
Features	Good Rigidity
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.250	g/cm³	ASTM D792

MECHANICAL	Nominal value	Unit	Test method
tensile strength
22℃，12 mm	14.0	MPa	ASTM D638
Bending modulus
22℃，12 mm	3000	MPa	ASTM D790
bending strength
22℃，12 mm	15.0	MPa	ASTM D790

Supplementary information	Nominal value	Unit	Test method
Reinforcing Mat Weight	600	g/m²

THERMAL	Nominal value	Unit	Test method
Linear coefficient of thermal expansion
MD：12 mm	1.5E-5	1/℃	ASTM D696
Thermosetting components
Component A	按重量计算的混合比: 140
Component B	按重量计算的混合比: 100

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.