| Baytec 352 is a two-component, one-shot system that yields a solid polyurethane elastomer with good mechanical properties in the hardness range of Shore 75A to 90A. As with any product, use of Baytec 352 in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | TSU |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| elastic body | Nominal value | Unit | Test method |
| tensile strength | |||
| fracture | 16.6 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 410 | % | ASTM D412 |
| tear strength | |||
| — | 47.8 | kN/m | ASTM D624 |
| cracking | 13 | kN/m | ASTM D1938 |
| Compression deformation | |||
| 70℃，22 hr | 84 | % | ASTM D395B |
| Basho’s elasticity | 33 | % | ASTM D2632 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| Part C | 按重量计算的混合比: 5.0 | ||
| Component A | 按重量计算的混合比: 33 | ||
| Component B | 按重量计算的混合比: 100 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 76 | ASTM D2240 | |
| Taber abraser | |||
| 1000 cycles | 37.0 | mg | ASTM D3489 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Isocyanate |
| 4. Polyol |
| 5. 1,4 Butone Diol |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |