| 60-Minute Toughened Resin Infusion System Room Temperature, Low Viscosity Epoxy Resin System Applications BCC Products XP 2014-003R/H is a 60-minute, very low viscosity—yet tough—system for the production of composite parts or tools using an infusion process such as Vacuum Assisted Resin Transfer Molding, RTM or other infusion processes.&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low Viscosity |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | < 0.10 | % | |
| MD | 0.15 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| — | 49 | ℃ | |
| — | 70 | ℃ |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Weight Mix Ratio (PBW) | |||
| Resin | 100 | ||
| Hardener | 18 | ||
| viscosity | |||
| 24℃ | 0.015 | Pa·s | |
| 24℃ | 0.13 | Pa·s | |
| 24℃ | 0.65 | Pa·s | |
| Curing time | |||
| 80℃ | 8.0 | hr | |
| 24℃ | 24 | hr | |
| Gelation time | |||
| 24℃ | 55 to 75 | min |
| Cured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 80 | ASTM D2240 | |
| tensile strength | |||
| — | 56.2 | MPa | |
| — | 68.0 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cured 8 hrs at 80°C |
| 3. Cured 7 days at RT |
| 4. 176°F (80°C) Cure |
| 5. RT Cure |
| 6. Hardener |
| 7. Mixed |
| 8. Resin |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |