| About |
|---|
| Bergamid™ A70 H natural FD is a Polyamide 66 (Nylon 66) product. It is available in Europe.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 to 1.15 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23 ℃, 4 mm, injection molding | 3800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| 23 ℃, 4 mm, injection molding | 87.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃, 4 mm, injection molding | > 10 | % | ISO 527-2/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 2.5 | kJ/m² | |
| 23℃ | 5.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | > 200 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| Maximum operating temperature | |||
| Continuous | 100 | ℃ | |
| Short-term | 180 to 200 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 100 to 120 | kV/mm | IEC 60243-1 |
| Relative permittivity | 3.60 | IEC 60250 | |
| Dissipation factor | 0.026 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 270 to 290 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Hold pressure | 50.0 to 100 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |