| About |
|---|
| Bergamid™ A700 G25 H (f1) is a Polyamide 66 (Nylon 66) product filled with 25% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Characteristics include: Flame Rated RoHS Compliant&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | DIN 53479 |
| dimensional stability | 0.0 | % | ISO 2796 |
| K-Value | 74.0 to 78.0 | ||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 8500 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 170 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -30℃ | 9.0 | kJ/m² | ISO 179/A |
| 23℃ | 10 | kJ/m² | ISO 179/A |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 55 | kJ/m² | ISO 179 |
| 23℃ | 65 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 250 | ℃ | ISO 75-2/A |
| Maximum operating temperature | IEC 60216 | ||
| — | 130 | ℃ | IEC 60216 |
| short time | 220 | ℃ | IEC 60216 |
| Melting temperature | |||
| DSC | 261 | ℃ | ISO 3146 |
| 0.70 mm | 100 | ℃ | UL 746 |
| 1.5 mm | 100 | ℃ | UL 746 |
| 3.0 mm | 100 | ℃ | UL 746 |
| 0.70 mm | 90.0 | ℃ | UL 746 |
| 1.5 mm | 90.0 | ℃ | UL 746 |
| 3.0 mm | 90.0 | ℃ | UL 746 |
| Relative temperature index | UL 746 | ||
| Electrical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.70 mm | 90.0 | ℃ | UL 746 |
| 1.50 mm | 95.0 | ℃ | UL 746 |
| 3.00 mm | 100 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| — | 21 | kV/mm | ASTM D149 |
| — | 90 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 3.70 | IEC 60250 | |
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.70 mm | PLC 1 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 0.70 mm | PLC 4 | UL 746 | |
| 1.5 mm | PLC 4 | UL 746 | |
| 3.0 mm | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.70 mm, all colors | HB | UL 94 | |
| 1.50 mm, all colors | HB | UL 94 | |
| 3.00 mm, all colors | HB | UL 94 | |
| 3.00 mm, all colors | HB40 | IEC 60695-11-10, -20 | |
| 0.70 mm, all colors | HB75 | IEC 60695-11-10, -20 | |
| 1.50 mm, all colors | HB75 | IEC 60695-11-10, -20 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. ±0.03 g/cm³ |
| 3. 96% H2SO4 |
| 4. 0.039 in/min |
| 5. Continuous (GTP 50% Tensile) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |