| Bergamid™ A700 G35 U-SO is a Polyamide 66 (Nylon 66) product filled with 35% glass fiber. It is available in Africa & Middle East, Asia Pacific, or Europe. Characteristics include: Flame Rated RoHS Compliant Flame Retardant Halogen Free Heat Stabilizer&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Halogen free,Flame Characteristics,Heat Stabilized |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | DIN 53479 |
| Ash Content | 35 | % | ISO 3451 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23 ℃, 4 mm, injection molding | 11700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃, 4 mm | 184 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| Fracture, 23 ℃, 4 mm | 2.6 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 7.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 73 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| Maximum operating temperature | |||
| — | 120 | ℃ | |
| Short Time | 220 | ℃ | |
| Melting temperature | |||
| DSC | 261 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 80 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.015 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| Solution A | 400 to 550 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.9 to 3.0 mm, ALL | V-0 | Internal Method | |
| Igniting temperature of the hot wire | |||
| 3 mm | 960 | ℃ | IEC 60695-2-13 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. ±0.02 g/cm³ |
| 3. Type 1 |
| 4. Continuous (GTP 50% Tensile) |
| 5. 0.8 mm wire |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |