| About |
|---|
| PC/PETnatural lubrified with impact modified to gain improvements in injection and moulding generally used for pieces in conjunction with improved dimesional stability, better impact and good final surface with good HDT temperature for general industry.&& |
| Product Description | |
|---|---|
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Good Dimensional Stability,Lubricating,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 15 | g/10min | ISO 1133 |
| Water absorption rate | |||
| 23℃，24hr | 0.20 | % | ISO 62 |
| humidity | |||
| Pellets | 0.20 | % | ISO 1110 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 60 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 132 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 110 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 135 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+16 | ohms | IEC 60093 |
| Dielectric strength | 35 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | < 100 | mm/min | FMVSS 302 |
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 80 | ISO 868 | |
| Tensile modulus | 2100 | MPa | ISO 527-2 |
| tensile strength | 59.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 260 to 275 | °C | |
| Mold temperature | 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |