| Biodegradable compound for film extrusion Bio-Flex® F 1130 (prev. Bio-Flex® 219F)&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Biodegradable,Food contact compliance,Compostable |
| Availabilitys | Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Apparent density | 0.83 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 to 5.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 1.50 to 4.00 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 390 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 17.0 | MPa | ISO 527-2 |
| Bending modulus | 370 | MPa | ISO 178 |
| bending strength | |||
| 3.50% strain | 9.00 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | > 300 | % | ISO 527 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Water vapor transmittance | |||
| 45 µm | 70 | g/m²/24 hr | ISO 15106-3 |
| Oxygen transfer rate | |||
| 45.0 µm | 850 | cm³/m²/bar/24 hr | ISO 15105-2 |
| Nitrogen transfer rate | |||
| 45.0 µm | 160 | cm³/m²/bar/24 hr | DIN 53380-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 24℃ | 无断裂 | ISO 179/1eA | |
| Charpy Unnotch Impact strength | |||
| 24℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 89.0 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | > 155 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.30 | % | |
| Barrel 1 zone temperature | 160 | °C | |
| Barrel 2 zone temperature | 160 | °C | |
| Barrel 3 zone temperature | 165 | °C | |
| Barrel 4 zone temperature | 170 | °C | |
| Connector temperature | 170 | °C | |
| Melt temperature | < 190 | °C | |
| Nozzle temperature | 175 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |