| Biodegradable and compostable compound for film extrusion, certified according to EN 13432. Used in applications such as waste bags. Bio-Flex® F 1137 / Bio-Flex® Bin Liner (previously Bio-Flex® V 2877)&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Biodegradable,Compostable |
| Availabilitys | Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 to 4.5 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 1.50 to 3.50 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 310 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 15.5 | MPa | ISO 527-2 |
| fracture | 13.8 | MPa | ISO 527-2 |
| Bending modulus | 305 | MPa | ISO 178 |
| bending strength | |||
| 3.50% strain | 11.5 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 420 | % | ISO 527 |
| Fracture bending strain | No Break | ISO 178 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD，20 µm | 515 | MPa | ISO 527-3 |
| TD，20 µm | 420 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 20 µ m | 37.0 | MPa | ISO 527-3 |
| TD, yield, 20 µ m | 25.0 | MPa | ISO 527-3 |
| MD, fracture, 20 µ m | 36.0 | MPa | ISO 527-3 |
| TD, fracture, 20 µ m | 24.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| fracture | 430 | % | ISO 527-2 |
| MD, yield, 20 µ m | 290 | % | ISO 527-3 |
| TD, yield, 20 µ m | 460 | % | ISO 527-3 |
| MD, fracture, 20 µ m | 290 | % | ISO 527-3 |
| TD, fracture, 20 µ m | 460 | % | ISO 527-3 |
| Tear resistant vine ductility | ISO 6383-2 | ||
| Elmendorf – MD：20.0 µm | 100 | kN/m | ISO 6383-2 |
| Elmendorf – TD：20.0 µm | 290 | kN/m | ISO 6383-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 无断裂 | ISO 179/1eA | |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | > 155 | ℃ | ISO 3146 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |