Bio-Flex® F 6513

About
Bio-Flex® F 6513 Biodegradable compound for injection moulding.&&

Product Description
Generic	生物可降解聚合物
Material Status	Commercial: Active
Features	Renewable resources,Biodegradable
Availabilitys	Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.29	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	3.5 to 5.5	g/10min	ISO 1133
Melt Volume Rate
190℃，2.16 kg	3.00 to 5.00	cm³/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2600	MPa	ISO 527-2
tensile strength			ISO 527-2
yield	46.0	MPa	ISO 527-2
fracture	18.0	MPa	ISO 527-2
Tensile strain
fracture	22	%	ISO 527-2
Bending modulus	2790	MPa	ISO 178
bending strength
3.50% strain	63.0	MPa	ISO 178
Tensile Strain at Tensile Strength	4.8	%	ISO 527
Fracture bending strain	No Break	%	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	7.6	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	无断裂		ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Melting temperature
DSC	150 to 170	℃	ISO 3146

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	60	°C
Drying time	2.0 to 4.0	hr
Barrel rear temperature	150	°C
Barrel middle temperature	160	°C
Barrel front temperature	175	°C
Nozzle temperature	190	°C
Mold temperature	25 to 40	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.