Bio-Flex® S 5630

About
Bio-Flex® S 5630 is a Biodegradable Polymers (Biodeg Polymers) material. It is available in Europe for injection molding or thermoforming. Primary attribute of Bio-Flex® S 5630: Eco-Friendly/Green.&&

Product Description
Generic	生物可降解聚合物
Material Status	Commercial: Active
Features	Biodegradable
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.55	g/cm³	ISO 1183
Apparent density	0.90	g/cm³	ISO 60
Melt Flow Rate
190℃，2.16kg	10 to 12	g/10min	ISO 1133
Melt Volume Rate
190℃，2.16 kg	8.00 to 10.0	cm³/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2160	MPa	ISO 527-2
tensile strength
fracture	29.0	MPa	ISO 527-2
—	32.0	MPa	ISO 527
Tensile strain
fracture	9.0	%	ISO 527-2
Bending modulus	2400	MPa	ISO 178
bending strength
3.50% strain	46.0	MPa	ISO 178
Tensile Strain at Tensile Strength	6.00	vol%	ISO 527
Fracture bending strain	No Break	%	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	3.0	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	51	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	68.0	℃	ISO 75-2/B
Vicat Softening Temp	105	℃	ISO 306/A
Melting temperature
DSC	140 to 160	℃	ISO 3146

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Drying temperature	60	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.20	%
Barrel rear temperature	130	°C
Barrel middle temperature	150	°C
Barrel front temperature	170	°C
Nozzle temperature	180	°C
Mold temperature	30 to 65	°C
Drying temperature	60	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.20	%
Barrel 1 zone temperature	150	°C
Barrel 2 zone temperature	170	°C
Barrel 3 zone temperature	180	°C
Barrel 4 zone temperature	185	°C
Connector temperature	170	°C
Nozzle temperature	180	°C
Traction roller	20 to 50	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.