| Bio-Flex® S 9533 Biodegradable compound for injection moulding.&& |
| Product Description | |
|---|---|
| Generic | 生物可降解聚合物 |
| Material Status | Commercial: Active |
| Features | Renewable resources,Biodegradable |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 24 to 28 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4580 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 50.0 | MPa | |
| fracture | 30.0 | MPa | |
| Tensile strain | |||
| fracture | 8.0 | % | ISO 527-2 |
| Bending modulus | 4700 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | 4.0 | % | ISO 527-2 |
| Fracture bending strain | 3 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 37 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 63.0 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 150 to 170 | ℃ | ISO 3146 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 60.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 150 | °C | |
| Barrel middle temperature | 160 | °C | |
| Barrel front temperature | 175 | °C | |
| Nozzle temperature | 180 | °C | |
| Mold temperature | 30.0 to 65.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |