| About |
|---|
| BC-LBI08 is an agromaterial descending from the BioCérès range. It is a wheat flour-based product. BC-LBI08 is 100% biodegradable and from renewable ressources.&& |
| Product Description | |
|---|---|
| Generic | 生物可降解聚合物 |
| Material Status | Commercial: Active |
| Features | Renewable resources,Biodegradable,Compostable |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 to 1.39 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 170℃，2.16kg | 12 to 36 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 6.0 to 12 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 45.0 to 53.0 | ℃ | ISO 75-2/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 70 to 84 | ISO 868 | |
| Tensile modulus | 1510 to 2090 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 10.0 to 16.0 | MPa | ISO 527-2 |
| fracture | 7.00 to 13.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 0.80 to 1.4 | % | ISO 527-2 |
| Bending modulus | 1680 to 3120 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |