Biograde D-1M - SOLIAO

About
A Hybrid resin for rigid moulding and extrusion applications where Biodegradability is not required. For use in applications where the use of renewable resources are desired. Can be used for injection moulding BIOGRADE DM is based on a blend of thermoplastic starch (TPS) and polyolefin’s. This grade of resin is compatibilised to offer a high level of mechanical strength, good elongation properties and toughness. The resin is based on corn starch which is a renewable material. Applications Injection moulded products such as cutlery, toothbrushes, combs, shavers, golf-tees, etc. Stakes and pegs Horticultural products such as flower pots and stakes Injection moulded caps and closures Disposable plates and produce trays&&

About

A Hybrid resin for rigid moulding and extrusion applications where Biodegradability is not required. For use in applications where the use of renewable resources are desired. Can be used for injection moulding BIOGRADE DM is based on a blend of thermoplastic starch (TPS) and polyolefin’s. This grade of resin is compatibilised to offer a high level of mechanical strength, good elongation properties and toughness. The resin is based on corn starch which is a renewable material. Applications Injection moulded products such as cutlery, toothbrushes, combs, shavers, golf-tees, etc. Stakes and pegs Horticultural products such as flower pots and stakes Injection moulded caps and closures Disposable plates and produce trays&&

Product Description
Generic	生物可降解聚合物
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Renewable resources,Biodegradable,Good Tensile Strength
Availabilitys	Asia Pacific
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.08	g/cm³	ASTM D4883
Melt Flow Rate
230℃，2.16kg	7.0 to 7.5	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
tensile strength			ASTM D883
yield	> 13.0	MPa	ASTM D883
fracture	> 13.0	MPa	ASTM D883
Tensile strain
fracture	> 200	%	ASTM D883

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	31	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Melting peak temperature	90.0	℃	ASTM D3418

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Recommended maximum moisture content	0.20	%
Barrel middle temperature	170 to 180	°C
Barrel front temperature	150 to 160	°C
Nozzle temperature	180 to 190	°C
Processing (melt) temperature	160 to 165	°C
Mold temperature	10 to 15	°C
Recommended maximum moisture content	0.20	%
Melt temperature	160 to 165	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.