BIOPLAST® GF 106/02

About
BIOPLAST GF 106/02 is BIOTEC’s trademark for a completely new, plasticizer-free thermoplastic material. As a result of plasticizer absence no material built-up or steam occurs during processing of BIOPLAST GF 106/02. The material is extremely suitable for blown film extrusion, sheet film extrusion, tube extrusion and injection moulding of completely biodegradable products. The complete biodegradability and other functional properties enable the converter to advance in production areas, which could not be reached with traditional thermoplastic materials. The potato starch used for BIOPLAST GF 106/02 is native and not blended with plasticizer (which would be necessary for example to produce thermoplastic starch, TPS). BIOPLAST GF 106/02 therefore exhibits outstanding processing and performance characteristics as well as an excellent shelf life.&&

About

BIOPLAST GF 106/02 is BIOTEC’s trademark for a completely new, plasticizer-free thermoplastic material. As a result of plasticizer absence no material built-up or steam occurs during processing of BIOPLAST GF 106/02. The material is extremely suitable for blown film extrusion, sheet film extrusion, tube extrusion and injection moulding of completely biodegradable products. The complete biodegradability and other functional properties enable the converter to advance in production areas, which could not be reached with traditional thermoplastic materials. The potato starch used for BIOPLAST GF 106/02 is native and not blended with plasticizer (which would be necessary for example to produce thermoplastic starch, TPS). BIOPLAST GF 106/02 therefore exhibits outstanding processing and performance characteristics as well as an excellent shelf life.&&

Product Description
Generic	热塑性聚酯
Material Status	Commercial: Active
Features	Renewable resources,Good Printability,Biodegradable,Food contact compliance,Grease resistance,Soft,Gasoline resistance,Good coloring
Availabilitys	Europe

Technical Data
film	Nominal value	Unit	Test method
film thickness
test	> 10	µm	ISO 2286-3
tensile strength			ISO 527-3
MD，23℃，10 µm	20.0 to 35.0	MPa
TD，23℃，10 µm	20.0 to 35.0	MPa
Tensile strain			ISO 527-3
MD, fracture, 10 µ m	600 to 900	%
TD, fracture, 10 µ m	600 to 900	%
Water vapor transmittance
80 µm	120	g/m²/24 hr	DIN 53122
Oxygen transfer rate
80.0 µm	750	cm³/m²/bar/24 hr	DIN 53380-3

PHYSICAL	Nominal value	Unit	Test method
Density	1.20 to 1.30	g/cm³	ISO 1183
Apparent density	0.74 to 0.80	g/cm³	ISO 60
Melt Flow Rate
190℃，5.0kg	2.5 to 3.5	g/10min	ISO 1133
water content		%	Internal Method
Particle size	1.50 to 2.50	mm
Melt density	1.10 to 1.20	g/cm³	ISO 1133

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.