BIOPLAST® Wrap 100

About
BIOPLAST WRAP 100 is BIOTEC’s trademark for a completely new, plasticizer-free thermoplastic material, which allows the production of films with paper-like properties. As a result of plasticizer absence no material built-up or steam occurs during processing of BIOPLAST WRAP 100. The complete biodegradability and other functional properties of BIOPLAST WRAP 100 enable the converter to advance in production areas, which could not be reached with traditional thermoplastic materials or paper. The potato starch used for BIOPLAST WRAP 100 is native and not blended with plasticizer (which would be necessary for example to produce thermoplastic starch, TPS). BIOPLAST WRAP 100 therefore exhibits outstanding processing- and performance-characteristics as well as an excellent shelf life.&&

About

BIOPLAST WRAP 100 is BIOTEC’s trademark for a completely new, plasticizer-free thermoplastic material, which allows the production of films with paper-like properties. As a result of plasticizer absence no material built-up or steam occurs during processing of BIOPLAST WRAP 100. The complete biodegradability and other functional properties of BIOPLAST WRAP 100 enable the converter to advance in production areas, which could not be reached with traditional thermoplastic materials or paper. The potato starch used for BIOPLAST WRAP 100 is native and not blended with plasticizer (which would be necessary for example to produce thermoplastic starch, TPS). BIOPLAST WRAP 100 therefore exhibits outstanding processing- and performance-characteristics as well as an excellent shelf life.&&

Product Description
Generic	热塑性聚酯
Material Status	Commercial: Active
Features	Good heat sealing,Renewable resources,Low or no water absorption,Good Printability,Biodegradable,Food contact compliance,Good Ultrasonic Properties,Grease resistance,Good coloring
Availabilitys	Europe

Technical Data
film	Nominal value	Unit	Test method
film thickness
test	> 10	µm	ISO 2286-3
tensile strength			ISO 527-3
MD，23℃，10 µm	10.0 to 20.0	MPa
TD，23℃，10 µm	10.0 to 20.0	MPa
Oxygen permeability (wet) (20 µ m)	1000 to 1500	cm³/m²/24 hr	ASTM F1927
Water vapor transmittance
20 µm	150 to 190	g/m²/24 hr	ASTM F1249

PHYSICAL	Nominal value	Unit	Test method
Density	1.30 to 1.50	g/cm³	ISO 1183/A
Apparent density	0.85 to 0.95	g/cm³	ISO 60
Melt Flow Rate
190℃，2.16kg	10 to 20	g/10min	ISO 1133
water content		%	Internal Method
Particle size	1.00 to 3.00	mm
Melt density	1.20 to 1.40	g/cm³	ISO 1133

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.